EPOCROS™ WS-700 by Nippon Shokubai is a VOC-free adhesion promoter and crosslinking agent. It is a standard acrylic-based oxazoline functionalized reactive copolymer. The new crosslinking technology enhances the reactivity between oxazoline groups and carboxy groups through a heating and mixing process involving EPOCROS™ WS and a carboxy group-containing emulsion with a specific neutralization rate. It offers lower curing temperature, excellent storage stability, no peeling and long pot life for one packaging.
- It offers enhanced resistance to water, solvents and heat as well as superior film strength.
- It has higher reactivity than water-based epoxy, melamine and blocked isocyanate.
- It offers fast-drying, low-toxicity and high crosslinking density with a small amount added.
- EPOCROS™ WS-700 is suitable for polyethylene terephthalate (PET), oriented polypropylene (OPP) and polyvinyl chloride (PVC) applications.
- It is registered with CSCA (Japan), TSCA (USA), REACH EU and IECSC (China) regulations.
Product family:
Chemical family:
Product Type:
| Chemical Composition: | Visible After Login |
| Bio Based content | Visible After Login |
| Color | Visible After Login |
| Appearance | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
For which polymer
Availability
Product Status:Visible After Login
EPOCROS™ WS-700 properties
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Molecular Weight, Mn | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Molecular Weight, Mw | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Non-volatile Content | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Weight per Oxazoline (WPO) Equivalent | 0.0 Visible After Login | Visible After Login | Visible After Login |
| pH | 0.0 Visible After Login | Visible After Login | Visible After Login |