LNP™ THERMOCOMP™ Compound OF008A (Americas)
Supplied bySABIC- Last Updated on Jun 10, 2024
LNP™ THERMOCOMP™ Compound OF008A (Americas) by SABIC is a compound based on PFAS-free, 40% glass fiber reinforced, branched polyphenylene sulfide (PPS) resin. It shows high strength & stiffness. It is processed by injection molding. LNP™ THERMOCOMP™ Compound OF008A (Americas) is used in consumer applications like personal accessory, sports/leisures and home & commercial appliances. It is suitable for electrical industry and electronic applications such as mobile phones, computers and tablets and buildings & constructions.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Documents related to LNP™ THERMOCOMP™ Compound OF008A (Americas)
(2)
Compliance
No data available
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
Regional Availability:Visible After Login| Visible After Login| Visible After Login
LNP™ THERMOCOMP™ Compound OF008A (Americas) properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Arc Resistance | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High-Ampere Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High-Voltage Arc Tracking Rate (HVTR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Stress | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Wear Factor (K) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Heat Deflection Temperature (HDT), Unannealed | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
LNP™ THERMOCOMP™ Compound OF008A (Americas) Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Front Zone 3 Temperature | Visible After Login | Visible After Login | |
| Middle Zone 2 Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Rear Zone 1 Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |