Technical datasheet
LNP™ LUBRICOMP™ Compound DFL32 (Asia)
Supplied bySABIC- Last Updated on Jun 9, 2025
LNP™ LUBRICOMP™ Compound DFL32 (Asia) by SABIC is a polycarbonate (PC) resin reinforced with 10% glass fiber and 15% polytetrafluoroethylene (PTFE). Exhibits wear & friction resistance, It is suitable for processing by injection molding. LNP™ LUBRICOMP™ Compound DFL32 (Asia) is recommended for structural, outdoor, lawn & landscape, electrical devices & displays, sport/leisure, personal accessory, home & commercial appliances, electrical components, infrastructure, and consumer applications.
| Bio Based content | Visible After Login |
Documents related to LNP™ LUBRICOMP™ Compound DFL32 (Asia)
Compliance
No data available
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
LNP™ LUBRICOMP™ Compound DFL32 (Asia) properties
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Moisture Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
LNP™ LUBRICOMP™ Compound DFL32 (Asia) Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Front Zone 3 Temperature | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Middle Zone 2 Temperature | Visible After Login | Visible After Login | |
| Moisture Content | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Rear Zone 1 Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |