GENESTAR™ GP2450NH-2 by Kuraray is a standard, halogen-free polyamide (PA-9T) grade reinforced with 45% glass-fiber. It exhibits balance between mechanical properties and fluidity as existing halogen-based flame retardant brands. It is used in the manufacturing of board-to-cable connector, board-to-cable (FPC) connector and USB connector. GENESTAR™ GP2450NH-2 do not contain chlorine or bromine with V-0 flame retardant rating.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
GENESTAR™ GP2450NH-2 properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Loss Tangent | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Loss Tangent | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Loss Tangent | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Amp Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Amp Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Inclined-Plane Tracking | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Flammability Index (GWFI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Flammability Index (GWFI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Ignition Temperature (GWIT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Ignition Temperature (GWIT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Weld Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Bar-flow Length | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
GENESTAR™ GP2450NH-2 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Barrel Front Temperature | Visible After Login | Visible After Login | |
| Barrel Middle Temperature | Visible After Login | Visible After Login | |
| Barrel Rear Temperature | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Hold Pressure | Visible After Login | Visible After Login | |
| Hold Time | Visible After Login | Visible After Login | |
| Injection Pressure | Visible After Login | Visible After Login | |
| Injection Speed | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Moisture Content | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Nozzle Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |