XAREC™ S135 by Idemitsu Kosan is a light weight syndiotactic polystyrene (SPS) grade reinforced with 30% glass fiber. It offers good electrical, dielectric properties, moldability, dimensional & hydrolytic stability, good processability and low warpage.
- It exhibits good chemical-, water-, oil and long-term heat resistance.
- It can be processed by injection molding.
- Applications include japot parts (pump housing), IH pressure cooker parts? (steam contacted parts), coffee maker parts, plastics chopsticks, microwave containers?? and home appliances.
- It complies with RoHS & JHOSPA, UL 94 HB flame rating and is EU certified, FDA approved?.
- XAREC™ S135 also conforms to China and Taiwan regulations.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Documents related to XAREC™ S135
(14)
Compliance
| Food Contact Approval | Visible After Login |
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
XAREC™ S135 properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dissipation Factor | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Volume Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Specific Gravity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Transverse to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.45 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
XAREC™ S135 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Pre Drying Time | Visible After Login | Visible After Login | |
| Pre-Drying Temperature | Visible After Login | Visible After Login | |