BAYFLEX® XGT-100 (Glass filled) by Covestro is a two liquid component (modified diphenylmethane diisocyanate (MDI) and polyether polyol (152/100 by weight)) polyurethane elastomer grade, reinforced with 15% milled glass fiber (Owens Corning 737, 1/16 inch). It is processed by reaction injection molding (RIM). This grade offers extended gel time, excellent surface quality and high impact resistance. BAYFLEX® XGT-100 (Glass filled) is used in agricultural equipments, heavy-duty trucks, specialty transportation, and marine applications.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Appearance | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
BAYFLEX® XGT-100 (Glass filled) properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tear Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Viscosity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Viscosity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| NCO Content, Isocyanate Component | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Specific Gravity (Density), Isocyanate Component | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Specific Gravity (Density), Polyol Component | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Thickness | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Content, Polyol Component | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear Parallel to flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flash Point, Isocyanate Component, Closed Cup | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flash Point, Polyol Component, Closed Cup | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Heat Sag | 0.0 Visible After Login | Visible After Login | Visible After Login |
BAYFLEX® XGT-100 (Glass filled) Processing Guidelines
Injection Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Demold Time | Visible After Login | Visible After Login | |
| Shot Time | Visible After Login | Visible After Login | |
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Mold Temperature | Visible After Login | Visible After Login | |
| Polyol Temperature | Visible After Login | Visible After Login | |