XAREC™ S834 by Idemitsu Kosan is a light weight, flame retardant syndiotactic polystyrene (SPS) grade reinforced with 30% glass fiber. It is suitable for processing by injection molding.
- It provides high strength, low specific gravity, dimensional stability, and low water absorption.
- It offers improved chemical-, heat-, hydrolysis- and hot water resistance.
- It is suitable for electronic parts and electrical machinery applications.
- XAREC™ S834 complies with RoHS and UL 94 V-0 flame rating.
Product Type:
| Chemical Composition: | Visible After Login |
| Bio Based content | Visible After Login |
Documents related to XAREC™ S834
Compliance
| Food Contact Approval | Visible After Login |
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Conversion mode
For which polymer
Availability
Product Status:Visible After Login
XAREC™ S834 properties
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Arc Resistance | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Transverse to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.45 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dissipation Factor | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glass Content | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Mold Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Pre-Drying Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Volume Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |