TAROLOX 111 G7 DX02 is a flame retardant polyethylene terephthalate (PET) grade, reinforced with 33% glass fibers. Is a heat stabilized grade and contains release agent. Exhibits medium viscosity, low moisture absorption, good flow and dimensional stability, very good electrical- , mechanical- and thermal properties. Designed for injection molding process. Recommended for electrical applications. Complies with UNI EN ISO 9001:2008, ISO 9001:2008 Registration no., IT-3404, REACH Regulation (EC) No 1907/2006, 91/155/EEC - ISO 11014-1:1994(E), European Directive 2002/95/EC (RoHS Decree), UL746 B, UL746 A (HAI-HWI-CTI), UL 94 V-0 Flame Rating, Norm AFNOR NF F 16-101 and NF F 16-102 class I2-F2 (Grey color at 2mm).
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
| Appearance | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
TAROLOX 111 G7 DX02 properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Amp Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Amp Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Amp Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot-wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot-wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot-wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Flammability Index (GWFI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Limiting Oxygen Index (LOI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Reaction to Fire | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Smoke Index | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Granule Humidity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
TAROLOX 111 G7 DX02 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Rate of Injection | Visible After Login | Visible After Login | |