TAROFORCE PP 940-12 is an impact modified, chemically coupled polypropylene (PP) grade that is reinforced with 40% long glass fibers. It is a concentrated and UV stabilized grade. Exhibits very isotropic shrinkage, low warpage and emission, high strength, stiffness, heat deflection resistance and heat aging stability. TAROFORCE PP 940-12 shows high impact- and creep resistance due to the fiber skeleton structure formed in the parts. It can be processed by injection molding. It is recommended for automotive, furniture, seat modules, central console carriers, hatchback door modules, lift-gate modules, gear shift boxes, battery holders, instrument panel carriers, door module carriers and front end carriers. Complies with ISO 1043: PP-GF40.
| Bio Based content | Visible After Login |
| Color | Visible After Login |
| CI Name | Visible After Login |
| Appearance | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
TAROFORCE PP 940-12 properties
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Burning Rate | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame rating (UL 94) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Limiting Oxygen Index (LOI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Long Glass Fiber content | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Pellet Length | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
TAROFORCE PP 940-12 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Cushion | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time (Desiccant Dryer) | Visible After Login | Visible After Login | |
| Feed Temperature | Visible After Login | Visible After Login | |
| Front Temperature | Visible After Login | Visible After Login | |
| Injection Pressure | Visible After Login | Visible After Login | |
| Injection Rate | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Middle Temperature | Visible After Login | Visible After Login | |
| Moisture Content (Max) | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Nozzle Temperature | Visible After Login | Visible After Login | |
| Packing Pressure | Visible After Login | Visible After Login | |
| Rear Temperature | Visible After Login | Visible After Login | |
| Screw Revolving Speed | Visible After Login | Visible After Login | |
| Screw Revolving Speed (Diameter 40 mm) | Visible After Login | Visible After Login | |
| Screw Revolving Speed (Diameter 55 mm) | Visible After Login | Visible After Login | |
| Screw Revolving Speed (Diameter 75 mm) | Visible After Login | Visible After Login | |