No data available
LNP™ LUBRICOMP™ Compound BX03658N by SABIC is a wear resistant, styrene-acrylonitrile (SAN) reinforced with proprietary fillers. It exhibits good dimensional stability and tight dimensional tolerance. It is good for water meter applications. It is suitable for processing by injection molding. LNP™ LUBRICOMP™ Compound BX03658N is recommended for consumer applications, building components, sports & leisure, personal accessories, home- & commercial appliances, and electricals & electronics (mobile phone, computer, tablets).
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Documents related to LNP™ LUBRICOMP™ Compound BX03658N
Compliance
No data available
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
Regional Availability:Visible After Login| Visible After Login| Visible After Login
LNP™ LUBRICOMP™ Compound BX03658N properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Wear Factor (K) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Wear Factor (K) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Moisture Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Transverse to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.45 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
LNP™ LUBRICOMP™ Compound BX03658N Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Front Zone 3 Temperature | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Middle Zone 2 Temperature | Visible After Login | Visible After Login | |
| Moisture Content | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Rear Zone 1 Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |