LEXAN™ COPOLYMER EXL1444 (Asia) by SABIC is a PFAS-free, unreinforced polycarbonate (PC) siloxane copolymer with high impact resistance. It is a flame retardant, medium flow, heat-stabilized grade. Offers low temperature ductility (-40°C), excellent processability and release with shorter IM cycle times compared to standard PC. It is suitable for processing by injection molding. Recommended for electrical applications, food & beverage and mobile phones, computers and tablets. It is available in wide range of opaque colors. LEXAN™ COPOLYMER EXL1444 (Asia) can be possibly used in enclosures, food containers and wireless communications.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
Documents related to LEXAN™ COPOLYMER EXL1444 (Asia)
Compliance
| Food Contact Approval | Visible After Login |
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
LEXAN™ COPOLYMER EXL1444 (Asia) properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dissipation Factor | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dissipation Factor | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High-Ampere Arc Ignition (HAI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition (HWI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Surface Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Volume Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Flammability Index (GWFI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Limiting Oxygen Index (LOI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Yield Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Rockwell L | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Rockwell R | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Volume Flow Rate (MVR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Moisture Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption at Saturation | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Transverse to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Electrical | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical with Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| UL RTI, Mechanical without Impact | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
LEXAN™ COPOLYMER EXL1444 (Asia) Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Drying Time (Cumulative) | Visible After Login | Visible After Login | |
| Front Zone 3 Temperature | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Middle Zone 2 Temperature | Visible After Login | Visible After Login | |
| Moisture Content | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Nozzle Temperature | Visible After Login | Visible After Login | |
| Rear Zone 1 Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |
| Shot to Cylinder Size | Visible After Login | Visible After Login | |
| Vent Depth | Visible After Login | Visible After Login | |