ARLEN™ CH230N by Mitsui Chemicals is a flame retardant modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ CH230N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V0 flame rating.
Product family:
Chemical family:
Product Type:
| Appearance | Pellets |
Benefits
Heat Resistance, Good|
Water Absorption, Low to None|
Filled, Glass Fiber|
Flame retarded|
Rigidity, High|
Dimensional stability, Good|
Chemical resistance, Good
Compliance
| Certifications & Compliance | UL 94 |
Applications
Recommended markets
Applications
Conversion mode
Injection Molding
Availability
Product Status:COMMERCIAL
ARLEN™ CH230N properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 400 - 599 V | At 3.0 mm | |
| Dielectric Breakdown Voltage | 25 kV/mm | ASTM D149 | |
| Dielectric Constant | 4 | At 106Hz | ASTM D150 |
| Dissipation Factor | 0.013 | At 106Hz | ASTM D150 |
| Volume Resistivity | 1015 ohm-cm | ASTM D257 | |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL 94 | V0 | At 0.80 mm | UL 94 |
| Flame Rating, UL 94 | V0 | At 1.5 mm | UL 94 |
| Flame Rating, UL 94 | V0 | At 3.0 mm | UL 94 |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flexural Modulus | 11000 MPa | ASTM D790 | |
| Flexural Strength | 240 MPa | ASTM D790 | |
| Hardness, Rockwell M | 95 | ASTM D785 | |
| Impact Strength, Notched Izod | 80 J/m | ASTM D256 | |
| Tensile Elongation | 4 % | ASTM D638 | |
| Tensile Strength | 160 MPa | ASTM D638 | |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.4 % | At 2.00 mm | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.8 % | At 2.00 mm | ASTM D955 |
| Specific Gravity | 1.63 | ASTM D792 | |
| Water Absorption | 3 % | At 100°C, 24hr in water, 2 mm | ASTM D570 |
| Water Absorption | 0.3 % | At 23°C, 24hr in water, 2 mm | ASTM D570 |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Parallel to Flow | 3.0 x 10-5 1/°C | ASTM D696 | |
| CTE, Linear, Transverse to Flow | 6.0 x 10-5 1/°C | ASTM D696 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | ASTM D648 | |
| Glass Transition Temperature (Tg) | 85 °C | ||
| Melting Point | 310 °C | ||
| UL RTI, Electrical | 130 °C | At 0.80 mm | |
| UL RTI, Electrical | 130 °C | At 3.0 mm | |
| UL RTI, Electrical | 130 °C | At 1.5 mm | |
| UL RTI, Mechanical with Impact | 90 °C | At 0.80 mm | |
| UL RTI, Mechanical with Impact | 120 °C | At 3.0 mm | |
| UL RTI, Mechanical with Impact | 120 °C | At 1.5 mm | |
| UL RTI, Mechanical without Impact | 125 °C | At 0.80 mm | |
| UL RTI, Mechanical without Impact | 125 °C | At 1.5 mm | |
| UL RTI, Mechanical without Impact | 125 °C | At 3.0 mm | |
ARLEN™ CH230N Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Cylinder NH Temperature | 315 - 335 °C | ||
| Cylinder Zone 1 Temperature | 300 - 325 °C | ||
| Cylinder Zone 2 Temperature | 315 - 335 °C | ||
| Cylinder Zone 3 Temperature | 320 - 335 °C | ||
| Drying Temperature | 110 °C | ||
| Drying Time | 2 - 6 h | ||
| Hooper Temperature | 50 - 90 °C | Bottom | |
| Mold Temperature | 90 - 140 °C | ||
| Screw Revolution Speed | 150 rpm | ||
| Vent Depth | 10 µm | ||