LATILUB 87/28-20T by LATI is a self-lubricating, PTFE modified polycarbonate (PC) grade. Has accurately balanced additive content in order to avoid abnormal wear. Provides low friction coefficients and good sliding properties. Is suitable for processing by injection molding. Can be used in bushings, gears, cams and slides. LATILUB 87/28-20T complies with UL94 HB and V-1 flame rating.
| Bio Based content | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
LATILUB 87/28-20T properties
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating, UL94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flame Rating, UL94 | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Coefficient of Friction (COF) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Unnotched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Wear Factor (K) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
LATILUB 87/28-20T Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Cylinder Temperature | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Hot Runner Mold | Visible After Login | Visible After Login | |
| Linear Mold Shrinkage | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Pre Drying Time | Visible After Login | Visible After Login | |
| Speed | Visible After Login | Visible After Login | |
| Suggested Max. Regrind | Visible After Login | Visible After Login | |