Somos® PerFORM Reflect is a low viscosity stereolithography material developed for 3D printing parts for wind tunnel testing with particle imaging velocimetry (PIV). It produces strong, stiff and high-temperature resistant composite parts. It reduces post-processing by more than 30% as it eliminates the need for additional PIV coatings. Offers faster image processing, excellent detail resolution, improved surface quality and faster part finishing. Somos® PerFORM Reflect is used in wind tunnel testing for aerodynamic design optimization, high-temperature testing, electrical casings, tooling and automotive housings.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| CI Name | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
Regional Availability:Visible After Login| Visible After Login| Visible After Login
Somos® PerFORM Reflect properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Poisson’s Ratio | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Poisson’s Ratio | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Optical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Critical Exposure (EC) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Exposure (E10) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Slope of Cure-depth vs. In (E) curve, (Dp) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Viscosity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |