Technical datasheet
TOPAS® 8007S-04
Supplied byTopas Advanced Polymers (Polyplastics)- Last Updated on Oct 10, 2022
TOPAS® 8007S-04 by Topas Advanced Polymers (Polyplastics) is a glass-clear, high purity cyclic olefin copolymer (COC) grade. Recommended for healthcare and diagnostic applications.
- Used for syringes, cartridges, disposable diagnostic items and medical components.
- Exhibits high moisture barrier, excellent biocompatibility and high dimensional stability.
- Provides excellent alcohol-, acid- and alkali resistance.
- It is an ethylene oxide and gamma sterilizable grade and is suitable for processing by injection molding.
- TOPAS® 8007S-04 complies with ISO 10993 and US Pharmacopoeia XXIII-Class VI.
- It is listed with USA FDA under Drug Master File 12132 and Device Master File 1043.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
| Appearance | Visible After Login |
Compliance
| Food Contact Approval | Visible After Login |
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
TOPAS® 8007S-04 properties
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Volume Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame Rating | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Impact Strength, Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
Optical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Refractive Index | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Transmittance, Visible | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Dielectric Constant | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Ball Indentation | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Volume Flow Rate (MVR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption at Saturation | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Vapour Permeability | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
TOPAS® 8007S-04 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
Injection molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Feed Temperature | Visible After Login | Visible After Login | |
| Hold Pressure | Visible After Login | Visible After Login | |
| Injection Pressure | Visible After Login | Visible After Login | |
| Injection Speed | Visible After Login | Visible After Login | |
| Nozzle Temperature | Visible After Login | Visible After Login | |
| Pre Drying Temperature | Visible After Login | Visible After Login | |
| Pre Drying Time | Visible After Login | Visible After Login | |
| Residence Time | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |
| Zone 1 Temperature | Visible After Login | Visible After Login | |
| Zone 2 Temperature | Visible After Login | Visible After Login | |
| Zone 3 Temperature | Visible After Login | Visible After Login | |
| Zone 4 Temperature | Visible After Login | Visible After Login | |