ECOTRIA® R200 by SK Chemicals is a semi-crystalline copoleyster grade consisting of 30% of post-consumer recycled (PCR) materials. It offers transparency, clarity, slow crystallization rate and chemical resistance. It is used in cosmetic packaging, food and beverage packaging including heat shrinkable films. It also meets the requirements for food contact materials in Korea, Europe, US, China, and Japan. ECOTRIA® R200 complies with EU SVHC and RoHS.
| Bio Based content | Visible After Login |
Compliance
| Food Contact Approval | Visible After Login |
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Availability
Product Status:Visible After Login
ECOTRIA® R200 properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Rockwell | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Rockwell R | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Optical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Haze | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Transmittance, Visible | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Specific Gravity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Specific Gravity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |