HKR102 by Sasol is a polypropylene (PP) homopolymer grade. It contains antioxidant, processing stabilizer and acid scavenger. It exhibits low flow, superior mechanical properties and low water carry over during the extrusion process.
- It is suitable for processing by extrusion and injection molding.
- Used in extrusion applications such as woven industrial fabric for high strength products, carpet backing, sacks and bags.
- Other applications include flexible intermediate bulk containers(FIBC’s), packaging strapping and monofilaments.
- HKR102 is also recommended for injection molding applications such as domestic, industrial and general purpose articles.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Appearance | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
HKR102 properties
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Auto-ignition Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flash Point, Open Cup | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Ball Indentation | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
HKR102 Processing Guidelines
Extrusion Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Cooling Temperature | Visible After Login | Visible After Login | |
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melt Temperature | Visible After Login | Visible After Login | |