TORZEN® G2500HS1L NC01 PA66 Resin
Supplied byRadiciGroup- Last Updated on Sep 28, 2025
TORZEN® G2500HS1L NC01 PA66 Resin by RadiciGroup is a heat stabilized polyamide 66 (PA66) grade reinforced with 25 % glass fibers. Possesses high tensile strength and dimensional stability. Exhibits good machine feed and mold release. Suitable for processing by injection molding. TORZEN® G2500HS1L NC01 PA66 Resin is used in automotive, electrical/electronic and industrial applications. Complies with RoHS (European directive 2002/95/EC).
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| CI Name | Visible After Login |
| Appearance | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
TORZEN® G2500HS1L NC01 PA66 Resin properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption at Saturation | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Decomposition Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Decomposition Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
TORZEN® G2500HS1L NC01 PA66 Resin Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Cushion (range) | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Front Temperature | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Middle Temperature | Visible After Login | Visible After Login | |
| Moisture Content (Min) | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Nozzle Temperature | Visible After Login | Visible After Login | |
| Rear Temperature | Visible After Login | Visible After Login | |
| Screw Speed | Visible After Login | Visible After Login | |
| Vent Depth | Visible After Login | Visible After Login | |