Heraflex® E 3918 1000 NAT by Radici is a natural colored thermoplastic copolyester elastomer (COPE) grade. Possesses lowest modulus. Is suitable for processing by injection molding. Used in automotive, technical-industrial, sport and furnishings. Heraflex® E 3918 1000 NAT complies with ROHS 2002/95/CE.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
Heraflex® E 3918 1000 NAT properties
Elastomers properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Nominal Strain at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Electrical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Surface Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Volume Resistivity | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| 10% Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| 100% Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| 300% Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tear Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Abrasion | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
Heraflex® E 3918 1000 NAT Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Dew Point | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time (Desiccant Dryer) | Visible After Login | Visible After Login | |
| Injection Speed | Visible After Login | Visible After Login | |
| Maximum Water Content | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |