G-Lex P54A001N by GAIL is a high density polyethylene (HDPE) resin. It possesses bi-modal molecular weight distribution for better processability with good mechanical properties. It offers excellent creep strength, impact strength & high ESCR. It is recommended for pipe application like potable water (IS 4984), sprinkler irrigation (IS 14151) and sewerage (IS 14333). G-Lex P54A001N conforms to BIS regulation for food contact applications as well as natural resin designation PE EANA-50 T-006 of IS 7328:1992.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Compliance
| Food Contact Approval | Visible After Login |
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Availability
Product Status:Visible After Login
G-Lex P54A001N properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Environmental Stress Cracking Resistance (ESCR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |