Makroblend® UT235 M RE by Covestro is a 15% mineral filler reinforced PC+PET blend. It provides excellent dimensional stability. Possesses low coefficient of linear thermal expansion and easy release.
- It provides easy flow and can be processed by injection molding.
- Makroblend® UT235 M RE used for automotive exterior body parts, including radiator grilles and bumpers.
- It complies with regulations of ISCC PLUS Standard.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
Makroblend® UT235 M RE properties
Impact properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Impact Strength, Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strain at flexural strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength at 3.5% Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Puncture maximum force | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Impact Strength, Puncture | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Filler content | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Volume Flow Rate (MVR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption at Saturation | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| CTE, Linear, Normal to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| CTE, Linear, Parallel to Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 0.46 MPa (66 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Deflection Temperature at 1.8 MPa (264 psi) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
Makroblend® UT235 M RE Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Barrel Front Temperature | Visible After Login | Visible After Login | |
| Barrel Middle Temperature | Visible After Login | Visible After Login | |
| Barrel Nozzle Temperature | Visible After Login | Visible After Login | |
| Barrel Rear Temperature | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Melting Temperature | Visible After Login | Visible After Login | |
| Moisture Content | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
Injection molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Drying Time | Visible After Login | Visible After Login | |
| Vent Depth | Visible After Login | Visible After Login | |