CELANYL® B2 HH GF33 BK 269/UV/1 by Celanese is 33% glass fiber reinforced polyamide 66 grade. Offers heat-, UV- and weather stability, as well as low wear and friction. CELANYL® B2 HH GF33 BK 269/UV/1 is suitable for processing by injection-molding.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Appearance | Visible After Login |
Compliance
No data available
Applications
Recommended markets
No data available
Conversion mode
Availability
Product Status:Visible After Login
CELANYL® B2 HH GF33 BK 269/UV/1 properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Charpy | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Poisson's Ratio | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Poisson's Ratio | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Flow | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Linear Mold Shrinkage, Transverse | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
CELANYL® B2 HH GF33 BK 269/UV/1 Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Drying Temperature | Visible After Login | Visible After Login | |
| Melt Temperature | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
Injection molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Drying Time | Visible After Login | Visible After Login | |
| Ejection Temperature | Visible After Login | Visible After Login | |
| Processing Moisture Content | Visible After Login | Visible After Login | |
| Screw Tangential Speed | Visible After Login | Visible After Login | |