4LAC 25H23100 A-M is an anti-microbial, flame retardant acrylonitrile butadiene styrene (ABS) grade. Exhibits excellent processing properties, high dimensional stability, good mechanical strength, electrical properties, scuff- and abrasion resistance, low warpage and moisture absorption. Designed for injection molding process. Possible applications are computer housings, small appliances, automotive interior trim and medical components. Complies with UL 94 V-0 Flame Rating.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
| Color | Visible After Login |
| Appearance | Visible After Login |
Compliance
| Certifications & Compliance | Visible After Login |
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
4LAC® 25H23100 A-M properties
Flammability properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Flame rating (UL 94) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Glow Wire Test | 0.0 Visible After Login | Visible After Login | Visible After Login |
| High Current Arc Ignition | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hot Wire Ignition | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Hardness, Rockwell | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Modulus of Elasticity | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strain | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Ignition Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Absorption | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Heat Deflection Temperature (HDT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
4LAC® 25H23100 A-M Processing Guidelines
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Back Pressure | Visible After Login | Visible After Login | |
| Drying Temperature | Visible After Login | Visible After Login | |
| Drying Time | Visible After Login | Visible After Login | |
| Feed Throat Temperature | Visible After Login | Visible After Login | |
| Hold Pressure | Visible After Login | Visible After Login | |
| Injection Speed | Visible After Login | Visible After Login | |
| Maximum Screw Speed | Visible After Login | Visible After Login | |
| Moisture Content (Max) | Visible After Login | Visible After Login | |
| Mold Temperature | Visible After Login | Visible After Login | |
| Nozzle diameter | Visible After Login | Visible After Login | |
| Processing Temperature | Visible After Login | Visible After Login | |