Queo™ 7007LA by Borealis is an ethylene based octene-1 elastomer, produced in a solution polymerization process using a metallocene catalyst. It contains a low amount of processing stabilizer.
- It offers high clarity and low peak melting point.
- It is compatible with other polyolefins.
- Queo™ 7007LA is recommended for adhesive applications such as seal layers in lamination and flexible barrier films.
- It has a shelf life of 3 years.
| CAS Number | Visible After Login |
| Chemical Composition: | Visible After Login |
| Bio Based content | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Applications
For which system
Adhesives
Availability
Product Status:Visible After Login
Queo™ 7007LA properties
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Brittleness Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore A | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |