Queo™ 7007LA by Borealis is an ethylene based octene-1 elastomer. It is a modifier for polypropylene (PP). Exhibits high clarity and low peak melting point. It is produced in a solution polymerization process using a metallocene catalyst. It contains a low amount of processing stabilizers.
- Can be processed by extrusion.
- Shows versatile blending with other polyolefins in film, extrusion and molding applications.
- Queo™ 7007LA is recommended for surface protection film, high strength flexible films & cling film applications and for noise reduction in automotive applications.
- Suitable for producing halogen free flame retardant compounds and TPO compounds.
| CAS Number | Visible After Login |
| Chemical Composition: | Visible After Login |
| Bio Based content | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Conversion mode
For which polymer
Availability
Product Status:Visible After Login
Queo™ 7007LA properties
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Brittleness Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore A | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Viscosity, Mooney | 0.0 Visible After Login | Visible After Login | Visible After Login |