EVATANE® 28-25 by SK Functional Polymer is a soft, flexible ethylene vinyl acetate (EVA) random copolymer grade made by high pressure radicalar polymerization process. Possesses high VA content, good polarity, high cohesive strength and high fluidity. Exhibits good compatibility with most tackifying resins and waxes. EVATANE® 28-25 can be processed by film extrusion.
Product family:
Chemical family:
Product Type:
| CAS Number | Visible After Login |
| Bio Based content | Visible After Login |
Compliance
No data available
Applications
Recommended markets
No data available
Conversion mode
Availability
Product Status:Visible After Login
EVATANE® 28-25 properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore A | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vinyl Acetate content | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Ring & Ball Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
EVATANE® 28-25 Processing Guidelines
Other Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Visible After Login | Visible After Login | ||