SABIC® COHERE™ 8102 by SABIC is a metallocene polyolefin plastomer (POP) grade. It is an ethylene-octene copolymer produced via Nexlene Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has excellent processability. It is suitable for processing by blown film extrusion. Applications for SABIC® COHERE™ 8102 includes low temperature sealing layer for high value packaging such as low SIT, seal through contamination, toughness improvement.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
Regional Availability:Visible After Login| Visible After Login| Visible After Login
SABIC® COHERE™ 8102 properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| 1% Secant Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| 1% Secant Modulus, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| 1% Secant Modulus, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Film Tensile Strength at Break, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Film Tensile Strength at Break, TD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore A | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Dart Drop | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tear Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tear Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tear Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Elongation | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Optical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Haze | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break, TD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Viscosity, Mooney | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Glass Transition Temperature (Tg) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melting Point | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Sealing Initiation Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
SABIC® COHERE™ 8102 Processing Guidelines
Extrusion Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Barrel Temperature | Visible After Login | Visible After Login | |
| Blow up ratio | Visible After Login | Visible After Login | |