TIPELIN® 3100J by MOL Petrochemicals is a unimodal high-density polyethylene (HDPE) copolymer grade. It contains antioxidant and acid scavenger. It is suitable for processing by injection molding and compression molding.
- Offers good organoleptic properties and environmental stress crack resistance.
- It is free from slip agents.
- It is suitable for recycling by using modern recycling methods.
- TIPELIN® 3100J is recommended for caps and closures of carbonated soft drinks, beverage over caps and engineering and technical parts.
Product family:
Chemical family:
Product Type:
| Bio Based content | Visible After Login |
Compliance
No data available
Applications
Recommended markets
Applications
Conversion mode
Availability
Product Status:Visible After Login
TIPELIN® 3100J properties
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Flexural Modulus | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Hardness, Shore D | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Impact Strength, Notched Izod | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
Other properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Tensile Strength at Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Density | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Environmental Stress Cracking Resistance (ESCR) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Melt Mass-Flow Rate (MFR or MFI = Melt Flow Index or MI = Melt Index) | 0.0 Visible After Login | Visible After Login | Visible After Login |
Thermal properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Oxidation Induction Time (OIT) | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Vicat Softening Temperature | 0.0 Visible After Login | Visible After Login | Visible After Login |
TIPELIN® 3100J Processing Guidelines
Compression Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Processing Temperature | Visible After Login | Visible After Login | |
Injection Molding Processing Guidelines
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Melt Temperature | Visible After Login | Visible After Login | |