Cellophane™ 345DMS by Futamura is regenerated cellulose film (RCF), based on renewable wood pulp, coated on one side with nitrocellulose by a solvent process. It is heat-sealable on the coated side and has inherent anti-static properties. Its uncoated side is particularly receptive to inks, adhesive coatings or extrusion lamination. Possesses excellent dead-fold characteristics, high gloss and transparency. Used as a substrate in laminations accommodating a wide spectrum of packaging applications, e.g. condiments, dehydrated foodstuffs, freeze-pops, twist and bunch wrapping.
| Bio Based | Visible After Login |
| Bio Based content | Visible After Login |
| Color | Visible After Login |
Compliance
| Food Contact Approval | Visible After Login |
Applications
Recommended markets
Conversion mode
Availability
Product Status:Visible After Login
Regional Availability:Visible After Login| Visible After Login| Visible After Login
Cellophane™ 345DMS properties
Films properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Film Thickness - Tested | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Seal Strength | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Sealing Range | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Water Vapor Transmission Rate | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Yield | 0.0 Visible After Login | Visible After Login | Visible After Login |
Mechanical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| 1% Secant Modulus, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| 1% Secant Modulus, TD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Coefficient of Friction (COF), Dynamic | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Coefficient of Friction (COF), Static | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Elongation at Break | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength, MD | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Tensile Strength, TD | 0.0 Visible After Login | Visible After Login | Visible After Login |
Optical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Gloss | 0.0 Visible After Login | Visible After Login | Visible After Login |
| Haze | 0.0 Visible After Login | Visible After Login | Visible After Login |
Physical properties
| Properties | Value & unit | Test condition | Test method |
|---|---|---|---|
| Gas Transmission Rate, Oxygen | 0.0 Visible After Login | Visible After Login | Visible After Login |