Formulation
SBR Hot Melt Pressure Sensitive Adhesive
Last Updated on Jun 21, 2022
Typical formulation ingredients
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
| PHASE | INGREDIENTS | QuantitY | Actions |
|---|---|---|---|
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% |
End consumer benefits
No data available
Applications
Sub-applications
No data available
Application formats
No data available
No data available
Typical properties
20° Hold ( ½ inch x ½ inch contact area, 400 gm load), minutes 63
Initial Brookfield viscosity at 175°C, cps 14500
Brookfield viscosity at 175°C, cps (Aged 72 hrs at 150°C) 10000
Rolling ball tack, cm 0.3
Solids content, % 100
180° Peel adhesion (12 inches per min to steel), oz / inch 92
Initial Brookfield viscosity at 175°C, cps 14500
Brookfield viscosity at 175°C, cps (Aged 72 hrs at 150°C) 10000
Rolling ball tack, cm 0.3
Solids content, % 100
180° Peel adhesion (12 inches per min to steel), oz / inch 92