Formulation
Polyurea Adhesives (ii)
Last Updated on Jun 21, 2022
Typical formulation ingredients
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
| PHASE | INGREDIENTS | QuantitY | Actions |
|---|---|---|---|
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% |
End consumer benefits
No data available
Applications
Sub-applications
No data available
Application formats
No data available
No data available
Typical properties
Tear resistance, pli 288
Hardness, Shore A 91
100% Modulus, psi 502
200% Modulus, psi 611
Gel time, mins 9.5
300% Modulus, psi 720
Tensile strength, psi 714
(Mix Ratio: 1:1 by A:B by Volume)
Maximum elongation, % 450
Hardness, Shore A 91
100% Modulus, psi 502
200% Modulus, psi 611
Gel time, mins 9.5
300% Modulus, psi 720
Tensile strength, psi 714
(Mix Ratio: 1:1 by A:B by Volume)
Maximum elongation, % 450
Procedure
Visible After LoginVisible After Login Visible After Login-Visible After Login