Hot Melt Packaging Adhesives Based on Amorphous Polyolefin and Polyethylene (A)
Last Updated on May 2, 2025
Typical formulation ingredients
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
| PHASE | INGREDIENTS | QuantitY | Actions |
|---|---|---|---|
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% |
End consumer benefits
No data available
Applications
Sub-applications
No data available
Application formats
No data available
No data available
Typical properties
Set time, sec 4.5
T-peel strength to polyester, g/mm 67.5
Tensile strength, mPa 6.0
Ring and ball softening point, °C 141
Elongation at yield, % 23.7
Viscosity, cps @ 190°C 2100
T-peel strength to polyester, g/mm 67.5
Tensile strength, mPa 6.0
Ring and ball softening point, °C 141
Elongation at yield, % 23.7
Viscosity, cps @ 190°C 2100