Visible After Login
PHASE x
QuantitY x%
Actions
Formulation
2K, Modified Poly-BD Polyurethane Self-Adhesive (C)
Supplied ByCardolite -Last Updated on Jun 21, 2022
Typical formulation ingredients
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
| PHASE | INGREDIENTS | QuantitY | Actions |
|---|---|---|---|
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% |
End consumer benefits
No data available
Applications
Sub-applications
Application formats
No data available
No data available
Typical properties
Nylon Adhesion strength, MPa 1.0
Mixed viscosity, cps, at 25°C 7200
Polycarbonate Adhesion strength, MPa 1.9
Aluminum Adhesion strength, MPa 6.1
Water absorption at 25°C, % 14 Days 0.19
Water absorption at 25°C, % 7 Days 0.17
Hardness, Shore A 93
Tensile strength, MPa 7.0
Glass Transition Temperature, °C -77
PVC Adhesion strength, MPa 2.7
Elongation at break, % 77.2
Mixed viscosity, cps, at 25°C 7200
Polycarbonate Adhesion strength, MPa 1.9
Aluminum Adhesion strength, MPa 6.1
Water absorption at 25°C, % 14 Days 0.19
Water absorption at 25°C, % 7 Days 0.17
Hardness, Shore A 93
Tensile strength, MPa 7.0
Glass Transition Temperature, °C -77
PVC Adhesion strength, MPa 2.7
Elongation at break, % 77.2