2K, Modified Poly-BD Polyurethane Self-Adhesive (A)
Supplied ByCardolite -Last Updated on Jun 21, 2022
Typical formulation ingredients
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
Visible After Login
PHASE x
QuantitY x%
Actions
| PHASE | INGREDIENTS | QuantitY | Actions |
|---|---|---|---|
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% | |
| x | Visible After Login | x% |
End consumer benefits
No data available
Applications
Sub-applications
Application formats
No data available
No data available
Typical properties
Hardness, Shore A 92
Glass Transition Temperature, °C -75
Polycarbonate Adhesion strength, MPa 4.0
Water absorption at 25°C, % 14 Days 1.05
Elongation at break, % 42.5
PVC Adhesion strength, MPa 3.6
Mixed viscosity, cps, at 25°C 18000
Nylon Adhesion strength, MPa 1.4
Water absorption at 25°C, % 7 Days 0.78
Aluminum Adhesion strength, MPa 3.2
Tensile strength, MPa 3.5
Glass Transition Temperature, °C -75
Polycarbonate Adhesion strength, MPa 4.0
Water absorption at 25°C, % 14 Days 1.05
Elongation at break, % 42.5
PVC Adhesion strength, MPa 3.6
Mixed viscosity, cps, at 25°C 18000
Nylon Adhesion strength, MPa 1.4
Water absorption at 25°C, % 7 Days 0.78
Aluminum Adhesion strength, MPa 3.2
Tensile strength, MPa 3.5
Procedure
Visible After LoginVisible After Login Visible After Login-Visible After Login